PURAL PES 5L1191103T0A0 WHITE L L TS AM8 9010CA – QUALICOAT P-0476
Powder based on saturated carboxylated saturated polyester resins and hardeners alternative to TGIC selected for their external resistance characteristics.
Formulated with pigments and additives specifically chosen for their high resistance to UV rays and atmospheric agents. The specific feature of the series
ANTIMICROBIAL 8 is the presence in formulation of an inorganic antibacterial agent that gives the product marked characteristics
Properties and uses
Powder suitable for painting products in which the elimination and control of bacterial proliferation are of fundamental importance. To
example: machinery and equipment for the pharmaceutical or food industry, controlled contamination environments, sanitary equipment and furnishings and
hospital, equipment and products for the community, etc. In order to ensure good protection it is necessary to apply the powder at an average thickness of
Preparation of the support
The products adhere to all metal substrates as long as they are dry, clean and degreased. To prolong the resistance to corrosion it is advisable to carry out a
suitable chemical pretreatment of the surface according to the nature of the metal support.
Product applicable by electrostatic generator guns with voltages between 40-90 kV. Where present in the description the abbreviation “TS” the products are
can also be used with the use of triboelectric guns.
Differences in thickness of the applied paint can lead to variations in the surface appearance of the hardened paint. In the case of effect products
special the use of recovery is not recommended except for bonded products (BOND).
180 ° C x 20 ‘, 190 ° C x 15’, 200 ° C x 10 ‘(object temperature)
Characteristics of the hardened film (applications on steel sheet)
Erichsen drawing: & gt; = 5 mm ISO 1520
Cylindrical mandrel: & gt; = 4 mm ISO 1519
Impact test: & gt; = 2,5 Nm ASTM D2794
Buchholz hardness tester: & gt; = 80 ISO 2815
Adhesion test: Gt0 ISO 2409
Gardner 60 ° brilliance: 80-100 gloss ISO 2813
It has good resistance to most acids and bases at 10% and ethyl alcohol at room temperature of (25 ° C).
For specific requests it is necessary to contact our Customer Service.
Corrosion resistance (applications on Fe-phosphate bonder sheets)
Humidistat exposure: No alteration after 500 hours. ISO 6270
Accelerated corrosion Kesternich: No loss of adhesion after 10 cycles. ISO 3231
Salt Mist: After 1000 hours penetration & lt; 1 mm. ISO 9227
Accelerated aging QUV-B (313 nm) with QUV / SE cycle 4 h condenses at 40 ° C / 4 h irradiation 50 ° C (0.75 W / m² / nm. Application on Al sheet metal).
Test: Loss of gloss & lt; = 50% after 300 h. ISO 16474: 3
The product is guaranteed for 24 months from the production date if stored at a temperature not exceeding 30 ° C and in the original packaging.
Revision 3 / May. 2020
The above information is the result of careful research and our many years of experience, however taking into account the large number of
factors that contribute to the achievement of the values we describe, the user will take care of producing the optimal conditions necessary for the
achievement of the best result.
This product is intended for use in industrial plants only. The handling of the product by the user must
be carried out in accordance with the provisions for the use of powder paints and with what is reported in the safety data sheet sent together with the
product and to which you are referred.